The most diverse material in the world
Fiber composite materials offer high strength while maintaining low weight, which is unattainable with conventional materials.
The ability to customize stiffness in any direction, ranging from elastic to highly rigid, opens up limitless possibilities for the use of fiber composite materials.
Compared to metallic structures, fiber composite materials provide unparalleled weight reduction, making them ideal for lightweight construction.
In comparison to conventional materials, fiber composite materials have a longer lifespan as they fatigue significantly slower.
In dynamic environments, fiber composite components offer vibration damping capabilities up to ten times greater than metallic materials.
For temperature-sensitive applications, fiber composite materials provide the advantage of adjustable thermal expansion.
The high resistance to many chemicals makes fiber composite materials ideal for use in challenging environments.
The radiation transparency of fiber composite materials enables their use in medical applications.
When fire protection is crucial, fibers with already good fire-resistant properties can be combined with fire-resistant resins.
Matrix:
Büfa Firestop S440
3 layers of Saertex LEO type Q-E-821 g/m²
Tempering
no
Tensile strength [MPa]
332.8
Elongation at break [%]
2.4
E-modulus [MPa]
19248
Bending strength [MPa]
508.4
Bending elongation [%]
3.7
Flexural modulus [MPa]
15239
Matrix:
Büfa Firestop S440
Reinforcement:
3 layers of Saertex LEO type Q-E-821 g/m²
Tempering
6 hours 80°C
Tensile strength [MPa]
335.3
Elongation at break [%]
2.5
E-modulus [MPa]
20927
Bending strength [MPa]
650
Bending elongation [%]
4.4
Flexural modulus [MPa]
16785
Matrix:
Büfa Firestop S440
Reinforcement:
3 layers Oschatz PD type KN G 810 M4
Tempering
no
Tensile strength [MPa]
329.9
Elongation at break [%]
2.7
E-modulus [MPa]
17966
Bending strength [MPa]
564.2
Bending elongation [%]
4.6
Flexural modulus [MPa]
13061
Matrix:
Büfa Firestop S440
Reinforcement:
3 layers Oschatz PD type KN G 810 M4
Tempering
6 hours 80°C
Tensile strength [MPa]
364.4
Elongation at break [%]
2.7
E-modulus [MPa]
18157
Bending strength [MPa]
638.5
Bending elongation [%]
5
Flexural modulus [MPa]
13931
Matrix:
Büfa Firestop S585
Reinforcement:
600 g/m² glass mat, roving, RTM-300/PP18/300
Tempering
no
Tensile strength [MPa]
97.57
Elongation at break [%]
2
E-modulus [MPa]
8857
Bending strength [MPa]
151.3
Bending elongation [%]
4.014
Flexural modulus [MPa]
6861